MXene molecular sieving membranes for highly efficient gas separation — TEI-tagged view

Li DingpersName, Yanying WeipersName, Libo LipersName, Tao ZhangpersName, Haihui WangpersName, Jian XuepersName, Liang-Xin DingpersName, Suqing WangpersName, Jürgen CaropersName, Yury GogotsipersName (2018date). “MXene molecular sieving membranes for highly efficient gas separation.” Nature Communicationstitle·j.

Object of study —

Research question — whether ordered MXeneterm interlayer channels enable high-performance gas separation

Contribution — ordered-subnanometer-channel MXeneterm membrane exceeding the permeability-selectivity upper bound

Full text — tagged

The reference list is not part of the text we hold for this paper. Our copy was extracted from the publisher's page and the bibliography did not survive that extraction, so the article below ends before its references. Nothing has been removed by us.

Abstract. Molecular sievingterm membranes with sufficient and uniform nanochannels that break the permeability-selectivity trade-offterm are desirable for energy-efficient gas separation, and the arising two-dimensional (2D) materials provide new routes for membrane development. However, for 2D lamellar membranesterm, disordered interlayer nanochannelsterm for mass transport are usually formed between randomly stacked neighboring nanosheets, which is obstructive for highly efficient separation. Therefore, manufacturing lamellar membranesterm with highly ordered nanochannel structures for fast and precise molecular sievingterm is still challenging. Here, we report on lamellar stacked MXeneterm membranes with aligned and regular subnanometer channels, taking advantage of the abundant surface-terminating groups on the MXeneterm nanosheets, which exhibit excellent gas separation performance with H 2 permeability >2200 Barrer and H 2 /CO 2 selectivity >160, superior to the state-of-the-art membranes. The results of molecular dynamics simulationsterm·mth quantitatively support the experimentsterm·mth, confirming the subnanometer interlayer spacing between the neighboring MXeneterm nanosheets as molecular sievingterm channels for gas separation. Two-dimensional materials show great potential for membrane technologies, but their disordered channels hinder their molecular sievingterm performance. Here, WangpersName, GogotsipersName and colleagues design a MXeneterm membrane with ordered nanochannels that exhibits an excellent H 2 /CO 2 gas separation performance. Introduction Gas separation with membrane technology is attractive because of its high efficiency, low energy consumption, and simple operation 1 – 3 . Membranes with high permeability and high selectivity are urgently required 3 . The recent use of two-dimensional (2D) materials 4 , 5 , such as graphene and graphene oxide (GO) 6 – 13 , zeolite or metal–organic framework (MOF) nanosheets 14 – 16 , has led to innovative membrane designs. Previous studies have shown that MOF nanosheets are promising for membrane assembly 15 , 16 and a pioneering breakthrough work on zeolite nanosheets based membrane was also conducted by Tsapatsis 14 , 17 – 19 , where the molecules were mainly transported through the intrinsic pores in the 2D nanosheets. But the types of zeolite or MOFs that can be easily exfoliated are rather limited due to the structural deterioration in exfoliation process 15 , 16 . Similarly, the monolayer graphene with artificial sub-nanopores created by selective etching or ion bombardment is emerged as selective membrane for gas separation or ion sieving 20 – 22 . However, it is difficult to fabricate the graphene sheets with controllable and uniform pores due to the stochastic nature, which limits the industrial applications. In contrast to the membranes with intrinsic or artificial pores on the nanosheets as the main molecular sievingterm channels, another kind of 2D laminar membrane has attracted increasing attention due to its simple preparation and easy to large-scale fabrication, in which the molecules are transported and sieved through the interlayer nanochannelsterm between the neighboring nanosheets 6 – 8 , 23 . Therefore, for the latter 2D laminar membranes, the stacking structure of the nanosheets strongly affects the separation performance 6 – 8 . For instance, a GO membrane with randomly stacked structure exhibited only Knudsen diffusion during gas separation, while a membrane with an ordered structure exhibited molecular sievingterm with a greatly increased gas separation factor 6 . Moreover, many other well-ordered GO laminates exhibited enhanced gas or water separation performance in terms of their selectivity and permeability compared to the disordered ones 7 , 8 . However, since the oxygen-containing functional groups that decorate the defects in GO sheets are difficult to control, random laminar structures are easily formed when such sheets are stacked into membranes 7 , 8 . Another young family of 2D materials named “MXenesterm” with the formula of M n +1 X n T X , are usually produced by selectively etching the A-group (mainly group IIIA or IVA elements) layers from M n +1 AX n phases ( n = 1, 2, or 3), where M is an early transition metal and X is carbon and/or nitrogen. More importantly, abundant of surface-terminating groups (T X : = O, –OH and –F) are formed evenly on the entire surface of the nanosheets during the etching and delaminating processes 24 – 31 . Interestingly, the variety of T X species can create open narrow nanochannels between the neighboring nanosheets in stacked MXeneterm laminates, making MXeneterm a promising material to assemble highly efficient membranes 27 . Here, exfoliated MXeneterm nanosheets were used as building blocks to construct 2D laminated membranes for selective gas separation for the first time, as demonstrated using a model system of H 2 and CO 2 . The MXeneterm membranes exhibit excellent performance in terms of the hydrogen permeability and H 2 /CO 2 selectivity, transcending the state-of-the-art membranes. Such high-permeability hydrogen-selective membranes are desired in many fields, such as hydrogen production and carbon dioxide capture. Results Preparation of MXeneterm nanosheets The most common MXeneterm, Ti 3 C 2 T X , is obtained after selectively etching Al from the corresponding MAX (Ti 3 AlC 2 ) phase using hydrochloric acid and lithium fluoride 24 – 26 , 29 , the structures are displayed in Supplementary Fig. 1 and explained in Supplementary Note 1 . The Tyndall scattering effect in the as-prepared MXeneterm colloidal suspension is clearly observed (Fig. 1a , inset, Supplementary Fig. 2 , and Supplementary Note 2 ). The scanning electron microscopy (SEM) and transmission electron microscopy (TEM) images (Fig. 1a and Supplementary Fig. 3 ) show that the exfoliated MXeneterm nanosheets are very thin and nearly transparent to the electron beams. High-resolution TEM (HRTEM) image and selected-area electron diffraction (SAED) patterns (Fig. 1b and Supplementary Figs. 4 and 5 ) indicate the hexagonal structure of the basal planes and high crystallinity of the MXeneterm flakes without obvious nanometer-scale defects or carbide amorphization. As indicated from the atomic force microscopy (AFM) measurements (Fig. 1c and Supplementary Fig. 6 ), most of the MXeneterm nanosheets have a uniform thickness of 1.5 nm with a lateral size of 1–2 μm. Considering that the theoretical thickness of a Ti 3 C 2 T X single layer is ~1 nm 29 , 32 , and MXeneterm nanosheets adsorb water and other molecules that also contribute to the total thickness, the 1.5-nm-thick nanosheet should be monolayer Ti 3 C 2 T X 26 , 32 . Fig. 1 Morphology and structure of exfoliated MXeneterm (Ti 3 C 2 T X ) nanosheets and stacked MXeneterm membrane. a SEM image of the delaminated MXeneterm nanosheets on porous anodic aluminum oxide (AAO) (scale bar, 1 μm). Inset is the Tyndall scattering effect in MXeneterm colloidal solution in water. b HRTEM image of the MXeneterm nanosheet with SAED pattern in the inset (scale bar, 5 nm, inset b , 5 nm −1 ). c AFM image of the MXeneterm nanosheet on cleaved mica. The height profile of the nanosheet corresponds to the blue dashed line (scale bar, 500 nm). Note that the adsorbed molecules, such as H 2 O, also contribute the detected thickness of 1.5 nm. d SEM image of the MXeneterm membrane surface (scale bar, 500 nm). Inset is a photograph of a MXeneterm membrane. e Cross-sectional SEM image of the MXeneterm membrane (scale bar, 1 μm). Inset is a tweezer bent membrane. f Cross-sectional TEM image of the MXeneterm membrane with 2D channels (scale bar, 10 nm). g XRD patterns of the MAX (Ti 3 AlC 2 ) powder and MXeneterm (Ti 3 C 2 T X ) membrane with inset of the magnified XRD pattern at low Bragg angles. h Illustration of the spacing between the neighboring MXeneterm nanosheets in the membrane Preparation of 2D MXeneterm membranes The MXeneterm membranes were fabricated using vacuum-assisted filtration on anodic aluminum oxide (AAO) support (Fig. 1a and Supplementary Fig. 7 ). After detaching the MXeneterm layers from the substrate, free-standing MXeneterm membranes were directly obtained with good flexibility (Fig. 1e and Supplementary Figs. 8 and 9 ). From the top-view SEM and AFM images (Fig. 1d and Supplementary Fig. 10 ), the membrane is determined to be intact, and the terminating groups were also detected on the MXeneterm membrane (see Supplementary Figs. 11 – 17 and Supplementary Tables 1 – 3 for the Fourier transform infrared spectroscopy (FTIR), thermogravimetric analysis (TGA), energy dispersive X-ray spectroscopy (EDX), and X-ray photoelectron spectroscopy (XPS) results). The cross-sectional SEM image and elemental distribution (Fig. 1e and Supplementary Figs. 13 – 15 ) indicate a homogeneous laminar structure throughout the membrane. The cross-sectional TEM images (Fig. 1f and Supplementary Fig. 18 ) reveal well-organized, highly ordered subnanometer channels resulting from the evenly distributed terminating groups on the MXeneterm nanosheet surface 30 , 33 , 34 . The sharp (002) peak with high intensity in the powder X-ray diffraction (XRD, Fig. 1g ) results further confirms the ordered stacking in the MXeneterm membrane. The (002) peak at 2 θ = 6.6° indicates the d -spacing of ~1.35 nm, based on Bragg’s law (Supplementary Fig. 19 , Supplementary Note 3 , and Supplementary Equation ( 2) ). After deducting the monolayer thickness of ~1 nm 29 , 32 , the free spacing between the neighboring MXeneterm nanosheets is estimated to be ~0.35 nm (Fig. 1h ), which could serve as a molecular sieve to separate gases by membrane permeation. Gas separation performance of 2D MXeneterm membranes The MXeneterm membranes were sealed into Wicke–Kallenbach permeation cells to measure the gas separation performance (Supplementary Figs. 20 and 21 ). For our MXeneterm membrane, the permeability of the small gas molecules (2164 Barrer for He and 2402 Barrer for H 2 ) is much higher than that of the gases with bigger kinetic diameters (Fig. 2a and Supplementary Table 4 ), showing a clear cutoff in between. The ideal selectivity (238.4) of the single-gas permeation and the separation factor (166.6) of the mixed-gas permeation of H 2 /CO 2 are much higher than the corresponding Knudsen coefficient (4.7). Obviously, the gas permeation is mainly dominated by the gas kinetic diameter rather than its molecular weight (Fig. 2a and Supplementary Fig. 22 ), known as the molecular sievingterm (size exclusion) mechanism. Very interestingly, the permeability of CO 2 (10 Barrer) is approximately half of N 2 (19 Barrer), although its kinetic diameter (0.33 nm) is 9% smaller than that of N 2 (0.364 nm). Here, adsorption modifies the molecular sievingterm process. Because CO 2 has a much larger quadrupole moment than N 2 , it interacts with the MXeneterm membrane stronger (the interaction energy values of MXeneterm with CO 2 and N 2 , as calculated by molecular dynamics (MD) simulations, are −175.1 and −97.5 kJ mol −1 , respectively, see Supplementary Note 4 and 5 ), which considerably suppress the CO 2 diffusion in the MXeneterm subnanometer channels 6 , 7 . The adsorption isotherms of the gases on the MXeneterm membranes at 25 °C also indicate a preferential adsorption of CO 2 compared to N 2 or other gases (Supplementary Fig. 23 ), even though the adsorption capacities of the MXeneterm nanosheets are quite small 15 , 16 , 35 . The adsorbed CO 2 molecules in the subnanochannels can even block the passing molecules and increase the resistance to CO 2 diffusion, while such phenomenon is absent for H 2 , resulting a high separation factor of H 2 /CO 2 . For O 2 , its kinetic diameter (0.346 nm) is just slightly smaller than the interlayer spacing of the MXeneterm membrane (0.35 nm). Although O 2 can pass through the subnanochannels in the membrane, but with a much larger mass transfer resistance due to the confinement of the neighboring MXeneterm nanosheets. That is why the O 2 permeability is significantly lower than that of much smaller molecules, such as He and H 2 . Fig. 2 MD simulations of the gas permeation through the MXeneterm membrane compared with the experimental results. a Single-gas permeabilities through a 2-μm-thick MXeneterm membrane as a function of the gas kinetic diameter at 25 °C and 1 bar. Inset shows the selectivity of H 2 relative to the other gases in both the single-gas and equimolar mixed-gas permeation studies. b Comparison of the experimental and MD simulated selectivities of H 2 /CO 2 and H 2 /N 2 in both the single-gas and mixed-gas permeations. c The number of gas molecules that passed through the MXeneterm membrane in MD simulation as a function of simulation time for single-gas permeation. For H 2 , only the first 10 ns of the simulation are shown because of its fast permeation. By contrast, only two molecules pass through the MXeneterm membrane during the 200-ns-long simulation for CO 2 or N 2 . The CO 2 curve fluctuates because of CO 2 adsorption–desorption on the MXeneterm membrane. d Simulation snapshots at 0, 30, 100, and 300 ns for two sets of mixed-gas permeation systems: (H 2 + CO 2 ) and (H 2 + N 2 ). Note that H 2 was modeled by united-atom force field. The MXeneterm membrane was composed of two nanosheets with a free spacing of 0.35 nm located in the middle of the simulation system. In the beginning ( t = 0 ns), 30 H 2 and 30 CO 2 (or N 2 ) molecules were present in the feed chamber, which permeated through the MXeneterm membrane to the evacuated permeate chamber. The details can be found in section of “Methods” Gas separation mechanism To elucidate the gas separation mechanism, two sets of atomistic MD simulations (total simulation time >5 μs) were performed to study the gas transport through the MXeneterm membrane, as schematically shown in Supplementary Fig. 24 16 , 36 . First, the confined diffusion coefficients of He, H 2 , CO 2 , O 2 , N 2 , and CH 4 in two neighboring MXeneterm channels with 0.35 nm free spacing were calculated by MD simulations (Supplementary Fig. 25 and Supplementary Note 4 ) 37 . The simulation yields a diffusivity ratio of 175:238:1.0:4.1:1.4:0.1. Furthermore, hundreds-nanosecond (ns)-long MD simulations were carried out to study the passage of the gas molecules through the MXeneterm membrane 16 , 36 . In simulations of single-gas permeation (Fig. 2b, c , Supplementary Fig. 26 , and Supplementary Note 5 ), the fluxes of H 2 , CO 2 , O 2 , and N 2 transporting from the feed to permeate chamber are 0.75, 0.0038, 0.0071, and 0.0063 molecule ns −1 , respectively (each value are estimated from the average of four 200-ns-long MD simulations, except for the H 2 flux) (Supplementary Table 5 ). The simulated selectivities of H 2 /CO 2 (200) and H 2 /N 2 (120) are comparable to their respective experimental values of 238 and 129 (Fig. 2b ). From the mixed-gas separation simulations (Fig. 2d ), the selectivities of H 2 /CO 2 (162) and H 2 /N 2 (90), averaged from four 300-ns-long MD simulations, are close to the corresponding experimental selectivities of 167 and 78 (Fig. 2b and Supplementary Table 6 ). Both the MD simulations and experimentsterm·mth show that the gas molecules with sizes much smaller than the free spacing between the neighboring nanosheets (e.g., H 2 and He) move through the membrane quickly. By contrast, the gas molecules with sizes larger (or only slightly smaller) than the free spacing (O 2 , N 2 , and CH 4 ) move 100 times slower because of the molecular sievingterm mechanism, resulting in gas separation selectivity above 100. For the gas molecule with specific adsorptive property, such as CO 2 , its interaction with MXeneterm considerably affects the gas transport rate, which further increases the H 2 /CO 2 selectivity. The quantitative agreement between the MD simulations and experimentsterm·mth indicates that molecular sievingterm occurs during gas separation through the MXeneterm membrane. Generally, terminations on the surface of a 2D membrane may affect the separation performance in some cases, therefore, another model using –F termination (i.e., Ti 3 C 2 F 2 ) has also been built to investigate the effect of different terminations on the MD simulated gas permeation (Supplementary Table 7 , Supplementary Fig. 27 , and Supplementary Note 6 ). The results show that there is no significant difference between the gas permeation in two simulation systems. Discussion Moreover, the gas separation performance of the MXeneterm membranes can be optimized by adjusting the membrane thickness, temperature, feeding H 2 concentration, and feed gas pressure (Fig. 3a, b , Supplementary Figs. 28 – 33 , and Supplementary Note 7 ). The MXeneterm membrane shows stable performance during a 700 h continuous separation of H 2 /CO 2 mixture (Fig. 3c ). No deterioration was observed even when the feed gas contained 3 vol% steam (Supplementary Fig. 34 ). And the MXeneterm membranes also show good reproducibility (Supplementary Table 8 ). Further, the 2-μm-thick MXeneterm membrane also exhibits tensile strength above 50 MPa and Young’s modulus of 3.8 GPa, showing good mechanical properties (Supplementary Fig. 35 and Supplementary Note 8 ). Compared with various previously reported membranes (Fig. 3d , Supplementary Table 9 , and Supplementary Note 9 ), the MXeneterm membrane exhibits both great H 2 permeability (>2200 Barrer) and high H 2 /CO 2 selectivity (>160), which considerably exceeds the latest upper bound of most current membranes. This promising separation performance is attributed to the regular subnanometer channels in the stacked MXeneterm membrane, and the pivotal role of the regular structure in separation have also been further verified using MD simulation (Supplementary Note 6 ). Fig. 3 Gas separation performance of the MXeneterm membrane. a Single-gas permeabilities through the MXeneterm membranes with different thicknesses at 25 °C and 1 bar. b H 2 /CO 2 separation performance of a 2-μm-thick MXeneterm membrane as a function of temperature in the equimolar mixed-gas permeation. c Long-term separation of equimolar H 2 /CO 2 mixture through a 2-μm-thick MXeneterm membrane at 25 °C and 1 bar. d H 2 /CO 2 separation performance of the MXeneterm membrane compared with state-of-the-art gas separation membranes. The black line indicates the Robeson 2008 upper bound of polymeric membranes for H 2 /CO 2 separation 58 , and the orange dashed line represents the 2017 upper bound of the best current membranes for H 2 /CO 2 separation. Information on the data points is given in Supplementary Table 9 The 2D structure and tunable physicochemical properties of MXeneterm offer an exciting opportunity to develop a new class of molecular sievingterm membranes. Considering that more than 30 MXenesterm are already available 30 and dozens more can be produced, there is certainly plenty of room for improving the performance even further. This work is significant for gas separation, such as H 2 purification, e.g., in methanol reforming process, CO 2 capture for zero-emission fossil fuel power generation, H 2 recovery in ammonia production, etc. Furthermore, it also demonstrates a general concept for 2D membrane design with highly ordered nanochannels enabling fast and precise molecular sievingterm for mixture separation. Methods Preparation of the MXeneterm membranes The MXeneterm solution was synthesized as follows 29 : one gram of LiF (purchased from Aladdin) was dissolved in 20 ml HCl (6 M, purchased from Sinopharm Chemical Reagent Co., Ltd.,) solution in a 250 ml Teflon beaker. Then, 1 g Ti 3 AlC 2 (purchased from Beijing Jinhezhi Materials Co., Ltd.) was added to the solution with magnetic stirring at 35 °C for 24 h. The resulting product was washed using deionized (DI) water and centrifugated at 3500 rpm several times until the pH of the supernatant >6, and a clay-like sediment was obtained. The sediment was then dispersed in DI water with ultrasonication for 10 min in order to delaminate the MXeneterm flakes. Most of the unexfoliated MXeneterm was removed after centrifugation at 3500 rpm for 1 h. The concentration of the obtained MXeneterm solution was ~0.5 mg ml −1 . The MXeneterm membranes were prepared by filtering a certain amount of the MXeneterm solution on AAO (0.2 µm pore size and a diameter of 35 mm, purchased from Puyuannano Co., Ltd.) substrates using vacuum-assisted filtration (Supplementary Fig. 7 ). All membranes were dried at 70 °C for 24 h and could be easily detached from the substrate (Supplementary Fig. 8 ). During the membrane preparation process, Ar was used to prevent the oxidation. Characterization of the MXeneterm nanosheets and membranes SEM images were obtained using a Hitachi SU8220 device. The SEM elemental mapping analysis was conducted using an EDX (Oxford EDS, with INCA software). TEM images were obtained using a JEOL JEM-2100F microscope with an acceleration voltage of 200 kV. Elemental mapping in TEM was conducted using the Bruker EDS System. The XRD analysis was carried out using a Bruker D8 Advance with filtered Cu-Kα radiation (40 kV and 40 mA, λ = 0.154 nm); the step scan was 0.02°, the 2 θ range was 2–10° or 2–70°, and the step time was 2 s. FTIR was conducted by Bruker VERTEX 33 units in the wavenumber range of 400–4000 cm −1 . The XPS analysis was performed using an ESCALAB 250 spectrometer (Thermo Fisher Scientific) with monochromated Al-Kα radiation (1486.6 eV) under a pressure of 2 × 10 −9 Torr. The AFM images were obtained using a Bruker Multi Mode 8 scanning probe microscope (SPM, VEECO) in tapping mode. The TG measurement was analyzed on a Netzsch STA 449F3 instrument under the flow of N 2 . The adsorption isotherms of H 2 , CO 2 , N 2 , and CH 4 on the MXeneterm membranes were measured using a Micromeritics (ASAP 2460) instrument. The mechanical tests were performed using an Instron-5565 universal testing machine (USA). Gas permeation measurements All the gas permeation measurements were conducted by a homemade membrane module (Supplementary Fig. 20 ). Silicone gaskets were used to avoid the leakage and the direct contact between the stainless-steel module and membranes. The gas transport through the membrane was measured using the constant pressure, variable volume method. A calibrated gas chromatograph (GC, Agilent 7890A) was used to analyze the composition of the permeate gas. During single-gas permeation, a flow rate of 50 ml min −1 gas was used in the feed side of the membrane, and sweep gas with a flow rate of 50 ml min −1 was used to remove the permeated gas on the permeate side. During mixed-gas permeation, a gas mixture with a ratio of 1:1 was applied at the feed side of the MXeneterm membrane, and the total flow rate of the feed gas was maintained at 100 ml min −1 (each gas at 50 ml min −1 ). The gas flow was controlled using mass flow controllers (MFCs). The pressures on both the feed and permeate side were maintained at 1 bar. In most cases, N 2 was used as the sweep gas, except when using a N 2 -containing gas as the feed, then CH 4 was employed as the sweep gas. The gas separation measurements were carried out at different temperatures. The membrane module was packed with heating tape and thermocouple and temperature controller devices were used to control the temperature and heating rate (2 °C min −1 ). Feed gases containing different H 2 concentrations were obtained by adjusting the flow rates of H 2 and CO 2 , which were controlled using the MFCs and calibrated using a bubble flowmeter. Steam (3 vol%) was introduced into the feed gas after passing it through a water tank at room temperature. The different gas pressures at the feed side of the MXeneterm membranes were controlled with a back-pressure valve. All of the gas permeation tests were carried out at least three times. The permeability of each gas was calculated from the following equation 6 : 1 P = 1 Δ p × 273.15 273.15 + T × P atm 76 × L A × d v d t , where P is the permeability (1 Barrer = 1 × 10 −10 cm 3 cm cm −2 s −1 cmHg −1 at standard temperature and pressure (STP)); Δ p is the transmembrane pressure (atm); P atm is the atmospheric pressure (atm); T is the temperature (°C); L is the thickness of the membrane (cm); d v/ d t is the volumetric displacement rate in the bubble flowmeter; and A is the effective area of the MXeneterm membrane (1.13 cm 2 ). The selectivity of two components in the single-gas permeation (ideal selectivity) was calculated as follows: 2 α = P i P j , where P i and P j are the permeability of each component. The selectivity of two components in the mixed-gas permeation (separation factor) was calculated as follows: 3 α i ∕ j = y i ∕ y j x i ∕ x j , where x and y are the volumetric fractions of the corresponding component in the feed and permeate side, respectively 7 . MD simulations Classical MD simulations, which have been proven to be an efficient tool in similar studies 16 , 36 , 38 , were utilized to gain theoretical insight into the gas (e.g., H 2 , He, N 2 , O 2 , CO 2 , and CH 4 ) permeation through the MXeneterm membrane. Two sets of simulations were carried out: one to study the gas molecule permeation through the MXeneterm membrane (Supplementary Fig. 26 , denoted as the flux simulation) 16 , 36 , and another to calculate the gas diffusion coefficient in the MXeneterm subnanometer channels (Supplementary Fig. 25 , denoted as the confined diffusion simulation) 37 , 39 . In the flux simulation, 30 gas molecules were placed in the feed chamber on the left side of (along the z direction) the MXeneterm membrane (Ti 3 C 2 O 2 ) using a structure taken from the literature 40 . The free spacing between the MXeneterm nanosheets was ~3.5 Å (see main text in Fig. 1h ), and 2.4 wt% water as adsorbate was added randomly between the MXeneterm nanosheets, as determined from the experimentsterm·mth (see the experimental TG in Supplementary Fig. 12 ). In order to investigate the effect of the surface functional groups on gas separation, gas permeation through the MXeneterm membranes with another model (Ti 3 C 2 F 2 ) has also been simulated and simulations of gas permeation were conducted through the MXeneterm membrane again (H 2 and CO 2 as examples) (Supplementary Fig. 27 and Supplementary Table 7 ). The MXeneterm nanosheets were modeled by the UFF force field (FF) with QEq charge 41 , 42 , which has been proven to accurately simulate the interactions of gas molecules with nanoporous materials. The water was described using the SPC/E model 43 . The N 2 , O 2 , CO 2 , and CH 4 gas molecules were modeled using the TraPPE FF 44 , 45 , and the united-atom parameters of H 2 and He were taken from other publications 46 , 47 . These FF parameters have been proven to accurately simulate the transport of these five gases in nanoporous materials 39 , 48 – 50 . In both the flux or diffusion simulation, the system was subjected to a 500-step steepest-descent energy minimization. Then, a 200–300 ns (flux) or 40 ns (diffusion) NVT (constant particle number, volume and temperature) simulation was performed (leap-frog algorithm with a time step of 2 fs). The Nose–Hoover thermostat 51 was employed to maintain a constant simulation temperature of 300 K. The MXeneterm atoms were frozen in the simulations since the nanosheets were rather rigid. The short-range interactions were evaluated using a neighbor list of 10 Å that was updated every ten steps, and the Lennard–Jones interactions were switched off smoothly between 8 and 9 Å. A long-range analytical dispersion correction was applied to the energy to account for the truncation of these interactions 52 . The electrostatic interactions were evaluated using the reaction-field method 53 . During the flux simulation, the gas molecules passed through the membrane to the permeate chamber (along the z direction), driven by the concentration difference, and the flux was calculated as the ratio of the number of gas molecules passing through the membrane to the simulation time. The MXeneterm membrane was 5.5 nm × 5.3 nm in the primary simulation box, and a periodic boundary condition (PBC) was applied to the x – y direction (thus, the MXeneterm membrane was essentially infinite in the x– y direction). The z length of the flux simulation box was 32 nm, and the MXeneterm membrane (length ~5.3 nm) was placed approximately in the middle, leading to the feed chamber of ~12.6 nm long, and the permeate chamber of ~14.1 nm long. Considering the lateral size of the MXeneterm flakes in the experimentsterm·mth was 1–2 μm, confined diffusion simulations were also performed, in which six gas molecules (H 2 , He, N 2 , O 2 , CO 2 , and CH 4 ) diffused between two MXeneterm nanosheets (without the presence of a feed chamber or permeate chamber). These two MXeneterm nanosheets with a free spacing of 0.35 nm were essentially infinite since the PBC was applied during the MD simulations, although they were 5.5 nm × 5.3 nm in the primary simulation box. During the confined diffusion simulation, the gas molecules diffused in two neighboring MXeneterm nanosheets (a confined subnanochannel), and for each gas, a 40 ns NVT calculation was carried out and using the Einstein relation, 4 D = lim t → ∞ 1 6 t 1 N ∑ N k = 1 r k ( t ) - r k ( 0 ) 2 , where r k ( t ) is the position of the k th molecule at time t and N is the number of molecules. All MD simulations in this work were performed using the GROMACS 4.6.7 package 54 , 55 , while the simulation trajectories were analyzed using the GROMACS utilities and home-written codes. The interaction energies of the gas molecules with the MXeneterm nanosheets were calculated from the diffusion simulation trajectories. Figures of the simulated systems were produced using VMD software 56 . Each flux simulation (200 ns for the single-gas permeation of H 2 , N 2 , O 2 , CO 2 with 30 gas molecules in the simulation system; 300 ns for the mixed-gas permeation of H 2 + N 2 and H 2 + CO 2 with 60 gas molecules in the simulation system, 30 for each gas species) was repeated four times, and the averaged flux was reported. The flux simulations of the single-gas permeation (in which only one gas was used, e.g., H 2 , N 2 , O 2 , or CO 2 ) were also performed with a very long permeate cell (~60 nm, denoted as the long-box simulations) to mimic the experimentsterm·mth more closely. The long-box simulations yielded very similar results compared to the normal-box simulation with a 14.1 nm long permeate cell (except for H 2 in which the flux changed a little from 0.75 to 0.90 molecule ns −1 ). Thus, the flux simulation refers to the normal size box ( z length of the box = 32 nm, permeate cell length = 12.6 nm, permeate cell length = 14.1 nm, main text Fig. 2d and Supplementary Fig. 26 ) in this work unless otherwise specified. Each diffusion simulation (H 2 , He, N 2 , O 2 , CO 2 , and CH 4 ) was 40 ns long. Thus, the total simulation time was 5 μs or more (4 × 3 × 200 ns + 4 × 2 × 300 ns + 5 × 40 ns = 5 μs). See our previous publications for further simulation details 57 . Data availability The data sets generated and analyzed during the current study are available from the corresponding authors on reasonable request. Electronic supplementary material Supplementary Information